XYRON™ VT31Z
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Asahi Kasei Chemicals Corporation |
| Trademark: | XYRON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ANIDGL_XYRON-VT31Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XYRON™ VT31Z is a Polyphenylene Ether + PS (PPE+PS) product filled with 10% filler. It can be processed by injection molding and is available in Africa & Middle East, Asia Pacific, Europe, or North America. Primary characteristic: flame rated. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.16 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1(2.00 mm) | 0.40 to 0.60 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 0.060 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield, 23°C) | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 30 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2470 | MPa | ISO 178 |
| Flexural Stress (23°C) | 88.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2(23°C) | 7.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed | 100 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 96.0 | °C | ISO 75-2/A |
| CLTE - Flow (-30 to 65°C) | 6.0E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
| Volume Resistivity (23°C) | 1.0E+16 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.00 mm | V-1 | ||
| 1.50 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 100 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 250 to 290 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | 150x150x2 mm |
| 2 . | 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VENELENE® 2707AP | Poliolefinas Internacionales, C.A. (Polinter) | HDPE | VENELENE® |
| Bayblend® FR3030 | Covestro - Polycarbonates | PC+ABS | Bayblend® |
| ALTECH® PP-H A 1000/120 UV GY1076-12LWA | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |
| 3M™ Dyneon™ Fluoroelastomer FX 2530R | 3M Advanced Materials Division | Fluorelastomer | 3M™ Dyneon™ Fluoroelastomer |
| LONGLITE® PBT 3030-104FR | CCP Group | PBT | LONGLITE® PBT |