NORYL™ 6850C resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AMYWmB_NORYL-6850C-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
NORYL 6850C is a PPO+PS extrusion grade, it is optimized for blending with polystyrene resins. It is suitable for (microwavable) food packaging and is compliant with US and European food contact regulations. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.06 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/5.0 kg) | 40.0 | cm³/10min | ISO 1133 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.25 | % | |
| Equilibrium, 23°C, 50% RH | 0.060 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2540 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 70.0 | MPa | |
| Break | 70.0 | MPa | |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 5.0 | % | |
| Break | 5.0 | % | |
| Flexural Modulus 1 | 2580 | MPa | ISO 178 |
| Flexural Stress | 107 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² | |
| Notched Izod Impact Strength 3 | ISO 180/1A | ||
| -30°C | 2.0 | kJ/m² | |
| 23°C | 4.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4(1.8 MPa, Unannealed, 64.0 mm Span) | 125 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 151 | °C | ISO 306/A120 |
| -- | 143 | °C | ISO 306/B50 |
| -- | 145 | °C | ISO 306/B120 |
| CLTE | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | |
| Transverse : -40 to 40°C | 7.0E-5 | cm/cm/°C |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity (280°C, 1500 sec^-1) | 133 | Pa·s | ISO 11443 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 100 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Hopper Temperature | 60.0 to 80.0 | °C | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 280 to 300 | °C | |
| Nozzle Temperature | 260 to 280 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*4 sp=62mm |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYCOA Polyamide 4112 FR | Nycoa (Nylon Corporation of America) | Nylon 6 | NYCOA Polyamide |
| Capran® 996 | Honeywell | Nylon, Unspecified | Capran® |
| DURANEX® 702MS | Polyplastics Co., Ltd. | PC+PBT | DURANEX® |
| PolyBlend™ 1100-45A | AdvanSource Biomaterials Corp. | TPU Alloy | PolyBlend™ |
| Petrothene® GA501150X01 | LyondellBasell Industries | LLDPE | Petrothene® |