FORMULA P COMP 5220 M1 Z
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | Putsch Kunststoffe GmbH |
| Trademark: | FORMULA P |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AMVMwe_FORMULA-P-COMP-5220-M1-Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Mineral filled PP copolymer. Good melt flow. Antistatic and scratch resistant. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 14 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| Yield | 20.5 | MPa | ISO 527-2 |
| Fracture | 16.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 65 | % | ISO 527-2 |
| Flexural Modulus | 2100 | MPa | ISO 178 |
| Flexural Stress (3.5% Strain) | 53.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 8.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 66.0 | °C | ISO 306/B |
| Additional Information |
|---|
| Tensile Strength, ISO 527: 20.5 MPa |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 250 - 260 | °C | |
| Mold Temperature | 40.0 - 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PP 513MN40 | SABIC Americas, Inc. | PP Impact Copolymer | SABIC® PP |
| Ming Dih EPS FM | Ming Dih Group Corporation | PS (EPS) | Ming Dih EPS |
| Flontech® FT-M02-2 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| Ebalta AH 110 / TGS | Ebalta Kunststoff GmbH | Epoxy | Ebalta |
| Generic PC+Polyester | Generic | PC+Polyester | Generic |