SABIC® LDPE HP0323N
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | SABIC Americas, Inc. |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AL8uLM_SABIC-LDPE-HP0323N.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRODUCT DESCRIPTION: SABlC® LDPE HPO323N is a Low Density Polyethylene grade without slip and anti-block additives. It typically exhibits good melt strength and processability. Films typically exhibit good toughness, good tear strength and high bundling force. TYPICAL APPLICATIONS: Heavy duty bags, industrial shrink films, construction and agriculture films, bags & pouches. This product is not intended for use in medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.923 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.30 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (0.0500 mm) | 260 | MPa | ISO 527-2 |
| Tensile Stress (yield, 0.0500mm) | 10.0 | MPa | ISO 527-2 |
| Coefficient of Friction | > 80 | % | ISO 8295 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Blow-up Ratio | 2.50 - 4.00 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Film Thickness - Recommended / Available | 70 - 220 micron | ||
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 25.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 500 | % | ISO 527-3 |
| Dart Drop Impact (50 µm, Blown Film) | 250 | g | ASTM D1709 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 96.0 | °C | ISO 306/A50 |
| Melting Temperature (DSC) | 110 | °C | ISO 3146 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | ASTM D2457 | ||
| 20, 50.0 µm, blown film | > 15 | ASTM D2457 | |
| 60, 50.0 µm, blown film | > 50 | ASTM D2457 | |
| Haze (50.0 µm, Blown Film) | < 14 | % | ASTM D1003 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Properties have been measured on 50 micron thickness blown film extruded at melt temperature of 180°C with BUR of 2.5 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 - 220 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitacell EPS-361MM | Taita Chemical Company, Ltd. | PS (EPS) | Taitacell |
| HiFill® PA6/6 GF30 HS L | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| INEOS LDPE 17L430 | INEOS Olefins & Polymers Europe | LDPE | INEOS LDPE |
| Perlast® ICE G90LT | Precision Polymer Engineering Ltd. | Perfluoroelastomer | Perlast® |
| LEXAN™ LUX7630C resin | SABIC Innovative Plastics | PC | LEXAN™ |