GLAMIDE® TY-835TC
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | TOYOBO America, Inc. |
| Trademark: | GLAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AKtsTa_GLAMIDE-TY-835TC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
GLAMIDE®TY-835TC is a polyamide 66 (nylon 66) product that contains 20% mineral fillers. It is available in North America. Features include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.28 | -- | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | 25 | -- | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | ASTM D955 | |||
| 1.00 mm | 0.30 - 0.60 | -- | % | ASTM D955 |
| 3.00 mm | 0.60 - 1.0 | -- | % | ASTM D955 |
| Water Absorption (24 hr) | 0.50 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | ASTM D638 | |||
| Yield, -40°C | 100 | 96.0 | MPa | ASTM D638 |
| Yield, 23°C | 80.0 | 58.0 | MPa | ASTM D638 |
| Yield, 80°C | 48.0 | 40.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.2 | 8.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | |||
| -40°C | 6400 | 5600 | MPa | ASTM D790 |
| 23°C | 5300 | 3800 | MPa | ASTM D790 |
| 80°C | 3500 | 1600 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | |||
| Yield, -40°C | 160 | 153 | MPa | ASTM D790 |
| Yield, 23°C | 130 | 90.0 | MPa | ASTM D790 |
| Yield, 80°C | 80.0 | 57.0 | MPa | ASTM D790 |
| Compressive Strength (23°C) | 90.0 | 62.0 | MPa | ASTM D695 |
| Taber Abrasion Resistance (1000 Cycles, CS-17 Wheel) | 30.0 | -- | mg | ASTM D1044 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact | ASTM D256 | |||
| -40°C | 35 | 45 | J/m | ASTM D256 |
| 23°C | 53 | 20 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, not annealed | 245 | -- | °C | ASTM D648 |
| 1.8 MPa, not annealed | 160 | -- | °C | ASTM D648 |
| CLTE - Flow | 5.8E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | 1.0E+13 | ohms·cm | ASTM D257 |
| Dielectric Strength (2.00 mm) | 24 | 16 | kV/mm | ASTM D149 |
| Arc Resistance | 130 | 120 | sec | ASTM D495 |
| Comparative Tracking Index | 600 | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | HB | -- | UL 94 |
| Additional Information |
|---|
| 干燥 Comparative Tracking Index, IEC Method: >600 V |
| 调节后的 Comparative Tracking Index, IEC Method: >600 V |
| Injection | Dry | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 270 - 300 | °C | |
| Mold Temperature | 60.0 | °C | |
| Injection Pressure | 30.0 - 60.0 | MPa |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUPREME HIPS SH825 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME HIPS |
| HANWHA CLNA-8400 | Hanwha Chemical | LLDPE | HANWHA |
| K PP 9071 AP | Technovinyl Polymers India Ltd. | PP, Unspecified | K PP |
| Shinkolite MR | Mitsubishi Rayon Co., Ltd. | Acrylic (PMMA) | Shinkolite |
| Sylvin 8344-75 Brown 7438 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |