RAMSTER PF305G6
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | RAMSTER |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AKVPKO_RAMSTER-PF305G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS FIBER REINFORCED, P.B.T FOR INJECTION MOLDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 15 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow | 0.30 | % | ASTM D955 |
| -- | 0.30 | % | ISO 2577 |
| Water Absorption | |||
| Saturation | 0.50 | % | ASTM D570 |
| Saturated, 23°C | 0.50 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.10 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 8100 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Yield) | 130 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 8600 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 180 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 8.5 | kJ/m² | ISO 179 |
| 23°C | 12 | kJ/m² | ISO 179 |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | 75 | kJ/m² | ISO 179 |
| 23°C | 70 | kJ/m² | ISO 179 |
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| -30°C | 8.5 | kJ/m² | ISO 180 |
| 23°C | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, not annealed | 219 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, not annealed | 206 | °C | ASTM D648, ISO 75-2/A |
| Maximum operating temperature- Short Peaks Operation | 200 | °C | |
| Maximum Continuous Use Temperature | 130 | °C |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flammability | 15 | mm/min | FMVSS 302 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 225 | °C | ISO 11357-3, ASTM D3418 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+17 | ohms·cm | IEC 60093 |
| Dielectric Strength | 3.8 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.050 | % | |
| Rear Temperature | 235 - 255 | °C | |
| Middle Temperature | 240 - 260 | °C | |
| Front Temperature | 245 - 270 | °C | |
| Processing (Melt) Temp | 240 - 270 | °C | |
| Mold Temperature | 70.0 - 90.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Holding Pressure | 30.0 - 105 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 25 to 50 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NEXT REPROCESSED PC/ABS 830-300R | NEXT Specialty Resins, Inc. | PC+ABS | NEXT REPROCESSED |
| AFFINITY™ SQ 1503UE | The Dow Chemical Company | POP | AFFINITY™ |
| Fiberfil® PP-61/TC/20 | Fiberfil® Engineered Plastics Inc. | PP Copolymer | Fiberfil® |
| MACOMASS TPE MM-TPE O 1451 | MACOMASS Verkaufs AG | TPE | MACOMASS TPE |
| RTP 205 A TFE 5 HI | RTP Company | Nylon 6 | RTP |