Chemiton CEJ7NA 55
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | Franplast S.r.l. |
| Trademark: | Chemiton |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AI0a9M_Chemiton-CEJ7NA-55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SEBS based compound with good recovery and excellent machinability. Ideal for the production of gaskets of any kind. Application:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 90 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 55 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 3.50 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 650 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 20 | kN/m | ISO 34-1 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -30 to 90 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 0.0 | hr | |
| Rear Temperature | 170 to 200 | °C | |
| Middle Temperature | 175 to 205 | °C | |
| Front Temperature | 180 to 210 | °C | |
| Nozzle Temperature | 185 to 215 | °C | |
| Mold Temperature | 30.0 to 60.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ADDILENE H 526 N30 | ADDIPLAST | PP Homopolymer | ADDILENE |
| Laticonther 62 GR/50 | LATI S.p.A. | Nylon 6 | Laticonther |
| Karina BLACK PVC COMPOUND 806-48/ 1-H-ISE | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LG PMMA HI835HS | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |
| Softell TKG 300N G82732 | LyondellBasell Industries | PP Copolymer | Softell |