Chemlon® 530 GH
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Teknor Apex Company (Chem Polymer) |
| Trademark: | Chemlon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AHue3T_Chemlon-530-GH.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Chemlon® 530 GH is a Polyamide 66 (Nylon 66) material filled with glass fiber. It is available in Asia Pacific, Europe, or North America for injection molding. Primary attribute of Chemlon® 530 GH: Flame Rated. Typical application of Chemlon® 530 GH: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.36 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.25 to 0.45 | % | ASTM D955 |
| Water Absorption (24 hr) | 1.0 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 128 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 2.5 | % | |
| Break | 4.0 | % | |
| Flexural Modulus | 5520 | MPa | ASTM D790 |
| Flexural Strength | 176 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 91 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 229 | °C | ASTM D648 |
| Melting Temperature | 257 | °C | |
| CLTE - Flow | 5.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.00 mm) | 15 | kV/mm | ASTM D149 |
| Comparative Tracking Index (CTI) | 600 | V | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.810 mm) | HB | UL 94 | |
| Oxygen Index | 23 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 79.4 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Suggested Max Regrind | 25 | % | |
| Rear Temperature | 252 to 268 | °C | |
| Middle Temperature | 263 to 274 | °C | |
| Front Temperature | 268 to 285 | °C | |
| Nozzle Temperature | 268 to 285 | °C | |
| Processing (Melt) Temp | 263 to 282 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC V931 BLK588 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Sinpolene MBW1282 | Teknor Apex Asia Pacific PTE. LTD. | LDPE | Sinpolene |
| Unichem 9814 | Colorite Polymers | PVC, Unspecified | Unichem |
| AKROMID® B3 GF 45 1 black (3851) | AKRO-PLASTIC GmbH | Nylon 6 | AKROMID® |
| Osterlene® PPH-2.6-BOPP | Osterman & Company | PP Homopolymer | Osterlene® |