KEBATRON® PPS L2040G3
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | BARLOG plastics GmbH |
| Trademark: | KEBATRON® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AHpV0B_KEBATRON-PPS-L2040G3.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPS, linear,40% glass fiber reinforced, reduced residual chlorine |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.65 | g/cm³ | ISO 1183 |
| Water Absorption (Saturation, 23°C) | 0.020 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 14500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 145 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.2 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 35 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 265 | °C | ISO 75-2/A |
| Melting Temperature 1 | 285 | °C | ISO 11357-3 |
| CLTE - Flow | 2.2E-5 | cm/cm/°C | ISO 11359-2 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flammability Classification 2(0.800 mm) | V-0 | IEC 60695-11-10, -20 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| 2 . | UL Registered |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RIALOX® B 120 GF30 ST F V-0 natural | RIA-Polymers GmbH | PBT | RIALOX® |
| RTP 683 HB | RTP Company | ABS | RTP |
| BMC 620X | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| Aplax P2620GN | Ginar Technology Co., LTD. | PP, Unspecified | Aplax |
| Geon™ Vinyl Flexible XV3796 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |