Lupolen 5461 B Q 471 is a high density polyethylene (HDPE) powder with high melt viscosity for extrusion of peroxide crosslinked pipes (PE-Xa). Typical application: Crosslinked pipes, PE-Xa (peroxide) It is not intended for medical and pharmaceutical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.953 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/21.6 kg) | 10 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 132/30) | 49.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant (23°C) | 1100 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 28.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 8.0 | % | ISO 527-2/50 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | < 280 | °C |
| Extrusion instructions |
|---|
| Melt temperatures above 280 °C should be avoided to prevent potential degradation. In case higher temperatures are needed please contact LyondellBasell. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SI301G15 | RJM International, Inc. | PET | RJM |
| NaturePlast NP DU 101 | NaturePlast | Nylon 610 | NaturePlast |
| Exact™ 9371 | ExxonMobil Chemical | Plastomer | Exact™ |
| Edgetek™ AS-000/000 AS NC505 | PolyOne Corporation | ABS | Edgetek™ |
| Karina CRYSTAL CLEAR PVC COMPOUND -E 75/318-IS-RG | Karina Ind. e Com. de Plásticos Ltda | PVC, Rigid | Karina |