AKROMID® B28 GM 10/20 1 LA black (4790)
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AKRO-PLASTIC GmbH |
| Trademark: | AKROMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AGXGM0_AKROMID-B28-GM-10-20-1-LA-black-4790-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
AKROMID® B28 GM 10/20 1 LA black (4790) is a 10% glass fibre reinforced, 20% glass bead filled, heat stabilised, laser markable, easy flowing polyamide 6 with good surface and slight tendency to warp. Application areas are housings, handles and switches in the automotive- and electrical industry |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.35 | -- | g/cm³ | ISO 1183 |
| Spiral Flow | 90.0 | -- | cm | Internal Method |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.50 | -- | % | |
| Humidity Absorption - 62% RH (70°C) | 2.2 | -- | % | ISO 1110 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 5700 | 3000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break) | 110 | 60.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break) | 2.6 | 10 | % | ISO 527-2/5 |
| Flexural Modulus 1 | 5000 | -- | MPa | ISO 178 |
| Flexural Stress 2 | 170 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 4.0 | -- | kJ/m² | |
| 23°C | 4.0 | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 30 | -- | kJ/m² | |
| 23°C | 30 | 80 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 200 | -- | °C | ISO 75-2/A |
| Melting Temperature 3 | 222 | -- | °C | DIN EN 11357-1 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+5 | -- | ohms | IEC 60093 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Burning Rate 4(1.00 mm) | < 100 | -- | mm/min | FMVSS 302 |
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 10 K/min, DSC |
| 4 . | >1 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYPRO® BP2200 | YUHWA Korea Petrochemical Ind. Co., Ltd. | PP Copolymer | POLYPRO® |
| SABIC® HDPE B5411 | Saudi Basic Industries Corporation (SABIC) | HDPE | SABIC® HDPE |
| TARFLON™ #2500 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| UMERIT® 500F | UBE America, Inc. | LLDPE | UMERIT® |
| CP PRYME® Polypropylene PPC100NB-20M NAT | Chase Plastics Services Inc. | PP Impact Copolymer | CP PRYME® Polypropylene |