RTV-2 GI-184B/GI-Thixotropic A

Category:	Silicone Rubber, RTV-2 , Silicone Rubber, RTV-2
Manufacturer:	Silicones, Inc.
Trademark:	RTV-2
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	AGWfr9_RTV-2-GI-184B-GI-Thixotropic-A.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
GI-184B is a high strength, tin-catalyzed, RTV-2 silicone rubber, that can be made thixotropic (non-flowing) with the use of GI-Thixotropic Activator. It has a small amount of flow to allow for some air release when poured, trowelled, brushed or sprayed onto the pattern. It will attain sufficient thixotropy to build enough wall thickness for a good skin mold. GI-184B has been designed to work with silicone rubber spray equipment. GI-184B can be used with other GI Activators to give good flow characteristics so an initial skin coat may be applied over the pattern to eliminate any trapped air at the mold surface. Generally, the quick curing Activators (GI-Fast Catalyst or GI-Ultra Fast Catalyst) are used for this prime coat. GI-184 can be used with GI-1000A, GI-179A, GI-800A or GI-2020A to pour conventional molds (all mixed 100 to 10 by weight). GI-184 is not sensitive to inhibition,meaning it will cure at room temperature over virtually any surface. GI-184 is extremely useful for vertical or overhead applications where superior mechanical properties are required.

Message

GI-184B is a high strength, tin-catalyzed, RTV-2 silicone rubber, that can be made thixotropic (non-flowing) with the use of GI-Thixotropic Activator. It has a small amount of flow to allow for some air release when poured, trowelled, brushed or sprayed onto the pattern. It will attain sufficient thixotropy to build enough wall thickness for a good skin mold. GI-184B has been designed to work with silicone rubber spray equipment.
GI-184B can be used with other GI Activators to give good flow characteristics so an initial skin coat may be applied over the pattern to eliminate any trapped air at the mold surface. Generally, the quick curing Activators (GI-Fast Catalyst or GI-Ultra Fast Catalyst) are used for this prime coat. GI-184 can be used with GI-1000A, GI-179A, GI-800A or GI-2020A to pour conventional molds (all mixed 100 to 10 by weight). GI-184 is not sensitive to inhibition,meaning it will cure at room temperature over virtually any surface. GI-184 is extremely useful for vertical or overhead applications where superior mechanical properties are required.

General Information
Features	High Strength Low Flow Thixotropic
Forms	Liquid

Physical	Nominal Value	Unit
Specific Gravity	1.16	g/cm³
Shrinkage - Cured	0.10	%

Cured Properties	Nominal Value	Unit	Test Method
Coverage - Cured	0.860	cm³/g

Thermoset	Nominal Value	Unit	Test Method
Shelf Life	26	wk

Uncured Properties	Nominal Value	Unit
Color
-- ¹	Blue
-- ²	White
Viscosity
-- ³	0.40 to 0.60	Pa·s
-- ⁴	85 to 95	Pa·s
Curing Time	16 to 18	hr
Pot Life
-- ⁵	45 to 60	min
-- ⁶	90 to 120	min

Cured Properties	Nominal Value	Unit	Test Method
Shore Hardness ⁷(Shore A)	16 to 24
Tensile Strength	2.45 to 2.79	MPa	ASTM D412
Tensile Elongation at Break	430 to 480	%	ASTM D412
Tear Strength	14.0 to 17.5	kN/m	ASTM D624

Note Message
1 .	Activator
2 .	Base
3 .	Activator
4 .	Base
5 .	Mixed
6 .	Base
7 .	7 Days

Resin Grade	Manufacturer	Category	Trademark
SCHULAMID® 6 GF 30 HI WIT	A. Schulman Europe	Nylon 6	SCHULAMID®
Trademark PE LLB1918B	Trademark Plastics Corporation	LLDPE	Trademark PE
NORYL™ WCA955 resin	SABIC Innovative Plastics Asia Pacific	PPE+TPE	NORYL™
Borealis PP RF926MO	Borealis AG	PP Random Copolymer	Borealis PP
Hostacom TRC 453N E G32845	LyondellBasell Industries	PP Copolymer	Hostacom