MAJORIS DFR218
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AGShLX_MAJORIS-DFR218.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
DFR218 is a halogen flame retardant compound with UL 94 V0 / 5VA, intended for injection moulding. The product is available in natural (DFR218) but other colours can be supplied on request. The product is heat stability, contains metal deactivator. APPLICATIONS DFR218 is intended for the injection moulding of electrical component. DFR218 specifically designed to fulfil these norms such as:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.35 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 6.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.90 - 1.1 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 24.0 | MPa | ISO 527-2/50 |
| Fracture | 26.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 7.0 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2700 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 1.5 | kJ/m² | ISO 179 |
| 23°C | 2.0 | kJ/m² | ISO 179 |
| Notched Izod Impact (23°C) | 2.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 131 | °C | ISO 75-2/B |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-0 | UL 94 | |
| 3.20 mm | V-0 | UL 94 | |
| 2.40 mm | 5VA | UL 94 | |
| Glow Wire Flammability Index | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (2.00 mm) | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 250 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYMAN® (ABS) E/HI | A. Schulman Europe | ABS | POLYMAN® |
| RheTech Polypropylene T20P105-00FA | RheTech, Inc. | PP, Unspecified | RheTech Polypropylene |
| Nypol® PA B3 T30 NTLA010 NT314 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| BCC Resins BC 9040T | BCC Products Inc. | Silicone | BCC Resins |
| AURAPENE PPUFBK35 | Aurora Manufacturing Ltd | TPO | AURAPENE |