Durethan® BKV 240 H2.0 XCP 901510
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LANXESS GmbH |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AGDNsL_Durethan-BKV-240-H2-0-XCP-901510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 6, 40 % glass fibers, injection molding, impact modified, heat-aging stabilized |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.41 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 280°C, 2.00 mm 1 | 0.73 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.13 | -- | % | |
| Flow : 280°C, 2.00 mm 3 | 0.25 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.030 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | 6000 | MPa | ISO 527-2/1 |
| Tensile Stress (Break, 23°C) | 160 | 100 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C) | 5.5 | 11 | % | ISO 527-2/5 |
| Nominal Tensile Strain at Break (23°C) | -- | 10 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 10100 | 6300 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 235 | 125 | MPa | |
| 23°C 6 | 255 | 150 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.0 | 5.5 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 6-HI,GHR,14-110,GF40 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.12 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 17 | -- | kJ/m² | |
| 23°C | 28 | 40 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 110 | -- | kJ/m² | |
| 23°C | 110 | 130 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | |||
| -30°C | 17 | -- | kJ/m² | |
| 23°C | 28 | 40 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 95 | -- | kJ/m² | |
| 23°C | 95 | 110 | kJ/m² | |
| Multi-Axial Instrumented Impact Energy | ISO 6603-2 | |||
| -30°C | 4.70 | -- | J | |
| 23°C | 9.10 | -- | J | |
| Multi-Axial Instrumented Impact Peak Force | ISO 6603-2 | |||
| -30°C | 1100 | -- | N | |
| 23°C | 1450 | -- | N |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 203 | -- | °C | ISO 75-2/A |
| Melting Temperature 8 | 220 | -- | °C | ISO 11357-3 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC X4558 | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Makrolon® OD2015 | Covestro - Polycarbonates | PC | Makrolon® |
| Maxelast® P3850H | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Xuchuan XCW-6300T | Xuchuan Chemical (Suzhou) Co., Ltd | PUR, Unspecified | Xuchuan |
| Mafill® CF 4002 | Ravago Group | PP Copolymer | Mafill® |