Lustran® SAN Sparkle
| Category: | SAN , Styrene Acrylonitrile |
| Manufacturer: | Styrolution |
| Trademark: | Lustran® SAN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AFlM36_Lustran-SAN-Sparkle.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lustran SAN Sparkle resin is an injection molding grade of transparent SAN (styrene acrylonitrile) thermoplastic. The base resin used in the Lustran SAN Sparkle product is in chemical compliance with 21 CFR 181.32 (acrylonitrile copolymers and resins) for use in the manufacture of repeated-use houseware articles. Water-clear Lustran SAN Sparkle resin is the clearest, most colorless, and most transparent grade in the Lustran SAN product line. Lustran SAN Sparkle resin combines glass-like clarity, like an acrylic, with superior processing characteristics. It is available in water-clear (552190) tint. Lustran SAN Sparkle resin is used in applications where improved optical clarity is desired. Typical applications include housewares, cosmetic packaging, and personal care items. Lustran SAN Sparkle performs exceptionally well in applications that are subject to demanding environments. Finished products are resistant to heat deformation, scratching, and chemicals, such as foodstuffs, oils, greases, acids, alkalies, and petroleum products. Common solvents, such as MEK and THF, can be used for bonding Lustran SAN Sparkle. Parts molded out of Lustran SAN Sparkle resin also accept various methods of printing. As with any product, use of Lustran SAN Sparkle resin in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.07 | g/cm³ | ASTM D792 |
| Specific Volume | 0.930 | cm³/g | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.30 - 0.40 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 75 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3200 | MPa | ASTM D638 |
| Tensile Strength (Break) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.1 | % | ASTM D638 |
| Flexural Modulus | 3400 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 96.5 | MPa | ASTM D790 |
| Deformation Under Load 1(50°C, 28 MPa) | 1.50 | % | ASTM D621 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 21 | J/m | ASTM D256 |
| Unnotched Izod Impact (3.20 mm) | 160 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, unannealed, 12.7mm | 93.0 | °C | ASTM D648 |
| 1.8 MPa, annealed, 12.7mm | 102 | °C | ASTM D648 |
| Vicat Softening Temperature | 108 | °C | ASTM D1525 2 |
| CLTE - Flow | 6.8E-5 | cm/cm/°C | ASTM D696 |
| RTI Elec (1.57 mm) | 50.0 | °C | UL 746 |
| RTI Imp (1.57 mm) | 50.0 | °C | UL 746 |
| RTI (1.57 mm) | 50.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.57 mm, Clear) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.570 | ASTM D542 | |
| Transmittance (3200 µm) | 89.0 - 90.0 | % | ASTM D1003 |
| Haze (3200 µm) | 0.70 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| A | 82.0 - 88.0 | °C | |
| B | 71.1 - 76.7 | °C | |
| Drying Time | |||
| A | 2.0 | hr | |
| B | 4.0 | hr | |
| Suggested Max Moisture | < 0.20 | % | |
| Suggested Shot Size | 50 - 70 | % | |
| Suggested Max Regrind | 20 | % | |
| Rear Temperature | 165 - 180 | °C | |
| Middle Temperature | 185 - 195 | °C | |
| Front Temperature | 195 - 205 | °C | |
| Nozzle Temperature | 195 - 205 | °C | |
| Processing (Melt) Temp | 205 - 260 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C | |
| Injection Pressure | 68.9 - 138 | MPa | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 0.00 - 0.172 | MPa | |
| Clamp Tonnage | 2.8 - 5.5 | kN/cm² | |
| Cushion | < 3.18 | mm | |
| Screw L/D Ratio | 20.0:1.0 | ||
| Screw Compression Ratio | 2.5:1.0 |
| Injection instructions |
|---|
| Hold Pressure: 40 to 80% of Injection PressureScrew Speed: Moderate |
| Note Message | |
|---|---|
| 1 . | 24 hrs |
| 2 . | 标准 B (120°C/h) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANTEC PC S60R GF30 | Polykemi AB | PC | SCANTEC |
| THERMOLAST® K TC0GPN (Series: GP/FG) | KRAIBURG TPE | TPE | THERMOLAST® K |
| BorPEX™ HE1878 | Borealis AG | HDPE, HMW | BorPEX™ |
| LNP™ STAT-KON™ DEL329EP compound | SABIC Innovative Plastics Europe | PC | LNP™ STAT-KON™ |
| Thermec N™ 4314R30H | Technical Polymers, LLC | PPA | Thermec N™ |