ASTAGLAS™ MV825I
| Category: | Acrylic (PMMA) , Polymethyl Methacrylate Acrylic |
| Manufacturer: | Marplex Australia Pty. Ltd. |
| Trademark: | ASTAGLAS™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AE2dvg_ASTAGLAS-MV825I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ASTAGLAS™ MV825I is a toughened high heat resistance moulding grade of Poly(Methyl Methacrylate) in the ASTAGLAS™ range. Typical applications are tinted or solid colour components requiring heat resistance and moulded component strength. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.18 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 3000 | MPa | ASTM D638 |
| Tensile Strength 2(3.20 mm) | 65.0 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 15 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 2850 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 95.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 45 | J/m | ASTM D256 |
| Falling Ball Impact | 2.00 | J | ASTM D6717 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 6.40 mm) | 98.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 101 | °C | ASTM D1525 6 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.490 | ASTM D542 | |
| Transmittance (Total, 3200 µm) | 92.0 | % | ASTM D1003 |
| Haze (3200 µm) | < 2.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 to 90.0 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 200 to 220 | °C | |
| Middle Temperature | 210 to 230 | °C | |
| Front Temperature | 220 to 240 | °C | |
| Processing (Melt) Temp | 230 to 250 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Injection Pressure | 60.0 to 130 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.100 to 0.500 | MPa | |
| Screw Speed | 40 to 60 | rpm | |
| Clamp Tonnage | 5.0 to 9.0 | kN/cm² |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 5.0 mm/min |
| 3 . | 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Menzolit® SMC 0190 | Menzolit Ltd (UK) | Polyester, TS | Menzolit® |
| Sylvin 7868-80C Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| SUPREME Specialty PS SP6503 | Supreme Petrochem Ltd. | PS (HIPS) | SUPREME Specialty PS |
| CALP 4310GF | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| RONFALIN® ABS 1328 A | A. Schulman Europe | ABS | RONFALIN® |