Propafilm™ SLT80
| Category: | PP Alloy , Polypropylene Alloy |
| Manufacturer: | Innovia Films Ltd. |
| Trademark: | Propafilm™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ADzlsU_Propafilm-SLT80.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
High Speed Overwrapping Film with Shrink Tightening Properties Biaxially oriented polypropylene (BOPP) film co-extruded on both sides with heat sealable polyolefinic copolymers. SLT80 is suitable for use in the tobacco industry for both high speed overwrapping of unit packs and display outers where good pack appearance and wrap tightness are required. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Molding Shrinkage | Internal Method | ||
| Flow : 80°C, 1 min | 3.0 | % | |
| Flow : 120°C, 1 min | 7.0 | % | |
| Across Flow : 80°C, 1 min | 2.0 | % | |
| Across Flow : 120°C, 1 min | 10 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic, Outside/Outside | 0.30 | ||
| vs. Itself - Static, Outside/Outside | 0.40 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 2000 | µm | |
| Secant Modulus 1 | ASTM D882 | ||
| 1% Secant, MD | 2800 | MPa | |
| 1% Secant, TD | 3300 | MPa | |
| Tensile Strength 2 | ASTM D882 | ||
| MD : Yield | 180 | MPa | |
| TD : Yield | 210 | MPa | |
| Tensile Elongation 3 | ASTM D882 | ||
| MD : Break | 100 | % | |
| TD : Break | 90 | % | |
| Seal Strength 4 | 0.15 | N/mm | Internal Method |
| Seal Initiation Temperature 5 | 110 to 141 | °C | Internal Method |
| Oxygen Permeability (23°C, 0% RH) | 43 | cm³·mm/m²/atm/24 hr | ASTM F1927 |
| Water Vapor Transmission Rate | ASTM F1770 | ||
| 23°C, 85% RH | 1.1 | g/m²/24 hr | |
| 38°C, 90% RH | 6.5 | g/m²/24 hr | |
| Blocking Load 6 | 6.0 | g | Internal Method |
| Yield | 54.9 | m²/kg | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (20°) | 130 | ASTM D2457 | |
| Haze 7 | 1.3 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 10%/min |
| 2 . | 50%/min |
| 3 . | 50%/min |
| 4 . | 225°F; 1sec; 15lb/in² |
| 5 . | 2secs; 15psi |
| 6 . | 158°F; 200g; 2hrs |
| 7 . | Wide angle; 2.5° |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Visico™ ME4425 / Visico™LE4438 | Borealis AG | LDPE | Visico™ |
| U-polymer UG-100-20 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Natur-Tec® BF3001J | Natur-Tec - Northern Technologies International Corp | Biodeg Polymers | Natur-Tec® |
| Thermec N™ 4314CF40 | Technical Polymers, LLC | PPA | Thermec N™ |
| TOTAL Polystyrene Crystal 585T | TOTAL Refining & Chemicals | PS (GPPS) | TOTAL Polystyrene |