TAROMID B 280 G4 X2
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID B |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ABnOz1_TAROMID-B-280-G4-X2.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6, glass fiber reinforced 20%, UL94 V2 self extinguishing, good flow and good mechanical properties. Available: all colors, heat stabilized (H), release agent (W), and without PBDE/PBDF. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.40 - 0.55 | % | ASTM D955 |
| Transverse flow | 0.75 - 1.2 | % | ASTM D955 |
| Water Absorption | |||
| 23°C, 24 hr | 1.6 | % | ASTM D570, ISO 62 |
| Saturation | 7.4 | % | ASTM D570 |
| Saturated, 23°C | 7.4 | % | ISO 62 |
| Granule Humidity | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6400 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength (Break) | 110 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 3.4 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 6000 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 1(23°C) | 4.4 | kJ/m² | ASTM D256, ISO 179 |
| Notched Izod Impact (23°C, 3.20 mm) | 50 | J/m | ISO 180, ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 180 | °C | ASTM D648, ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 204 | °C | ASTM D1525, ISO 306/A50 4 2 |
| -- | 200 | °C | ASTM D1525, ISO 306/B50 5 3 |
| Ball Pressure Test (165°C) | Pass | VDE 0470 | |
| Melting Temperature | 222 | °C | ASTM D211, ISO 121 |
| CLTE - Flow (-30 to 30°C) | 4.2E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index (Solution A) | 300 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | UL 94 | |
| 3.00 mm | V-0 | UL 94 | |
| Glow Wire Ignition Temperature (2.00 mm) | 850 | °C | IEC 60695-2-13 |
| Oxygen Index | 30 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 - 90.0 | °C | |
| Pre-drying equipment | 80.0 - 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Pre-drying equipment | 3.0 | hr | |
| Processing (Melt) Temp | 230 - 250 | °C | |
| Mold Temperature | 80.0 - 90.0 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | 6x4x50 mm |
| 2 . | 速率 A (50°C/h), 压 力1 (10N) |
| 3 . | 速率 A (50°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Resiten® 112 | ITEN INDUSTRIES | Phenolic | Resiten® |
| Witcom HDPE 2007/492 | Witcom Engineering Plastics B.V. | HDPE | Witcom HDPE |
| NEXUS Reprocessed PPC 10/2 RBK | Nexus Resin Group, LLC. | PP Copolymer | NEXUS Reprocessed |
| 3M™ Dyneon™ PTFE Compound TF 6105N | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE Compound |
| Envir® PA66G33HL-BK0101 | Barnet | Nylon 66 | Envir® |