TOTAL Polyethylene HDPE 50100.1

Category:	HDPE, HMW , High Density (HMW) Polyethylene
Manufacturer:	TOTAL Refining & Chemicals
Trademark:	TOTAL Polyethylene
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	ABd7cy_TOTAL-Polyethylene-HDPE-50100-1.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

TOTAL Polyethylene 50100.1 is a high density (HMW) polyethylene material,. This product is available in North America and is processed by blow molding.

The main features of TOTAL Polyethylene 50100.1 are:

flame retardant/rated flame

Comply with REACH standard

high molecular weight

High resistance to environmental stress fracture (ESCR)

Good processability

Typical application areas include:

food contact applications

packing

industrial applications

General Information
Features	High ESCR (Stress Cracking Resistance) High molecular weight Impact resistance, good Workability, good Good melt strength Compliance of Food Exposure Medium hardness
Uses	Blow molding applications Industrial application Food packaging
Agency Ratings	ASTM D 4976-89-PE235 EC 1907/2006 (REACH) FDA 21 CFR 177.1520(c) 2.1 FDA 21 CFR 177.1520(c) 2.2
Forms	Particle
Processing Method	Blow molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	0.948	g/cm³	ASTM D792
Melt Mass-Flow Rate (MFR) (190°C/21.6 kg)	11	g/10 min	ASTM D1238
Environmental Stress-Cracking Resistance			ASTM D1693B
10% Igepal, molded, F50	120	hr	ASTM D1693B
100% Igepal, molded, F50	> 600	hr	ASTM D1693B

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength ¹(Yield, Compression Molded)	26.2	MPa	ASTM D638
Tensile Elongation ²(Break, Compression Molded)	600	%	ASTM D638
Flexural Modulus (Compression Molded)	1210	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact (3.18 mm, Compression Molded)	530	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Peak Melting Temperature	127	°C	ASTM D3418

Flammability	Nominal Value		Test Method
Flame Rating	HB		UL 94

Additional Information
Blow Molding Stock Temperature: 370 to 450°F

Extrusion	Nominal Value	Unit
Melt Temperature	193 - 249	°C

Note Message
1 .	Type 4, 51mm/min
2 .	Type 4, 51mm/min

Resin Grade	Manufacturer	Category	Trademark
RTP 205 TFE 15 SI	RTP Company	Nylon 66	RTP
TECHNYL STAR™ SX 218 V50 BLACK 38N-K	Solvay Engineering Plastics	Nylon 6	TECHNYL STAR™
NOVALAC RX®525	Vyncolit N.V.	Phenolic	NOVALAC
KOCETAL® K300EWBBK	Kolon Plastics, Inc.	Acetal (POM) Copolymer	KOCETAL®
Sylvin 6228-80 Black	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin