Lumiloy® GN2101F
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lumiloy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | ABRfvA_Lumiloy-GN2101F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection Molding Grade, Flame Retardent mPPO Description High Strength & Modulus, GF 10% Reinforcement, High Impact Strenght Application Electric and Electronic Parts |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (280°C/5.0 kg) | 8.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | Internal Method | ||
| Flow : 2.00 mm | 0.20 to 0.50 | % | |
| Flow : 3.00 mm | 0.30 to 0.50 | % | |
| Across Flow : 2.00 mm | 0.70 to 0.90 | % | |
| Across Flow : 3.00 mm | 0.60 to 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 78.5 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | 5.0 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 3730 | MPa | ASTM D790 |
| Flexural Strength 4(Break, 3.20 mm) | 127 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 120 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 490 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 127 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-1 | Internal Method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 110 | °C | |
| Drying Time | 5.0 to 6.0 | hr | |
| Suggested Max Moisture | > 0.030 | % | |
| Rear Temperature | 260 to 300 | °C | |
| Middle Temperature | 270 to 310 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Nozzle Temperature | 265 to 305 | °C | |
| Processing (Melt) Temp | 280 to 320 | °C | |
| Mold Temperature | 60.0 to 110 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® B 216 NATURAL D | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| NYLAFORCE® dynamic B 50 | LEIS Polytechnik - polymere Werkstoffe GmbH | Nylon 6 | NYLAFORCE® dynamic |
| En Chuan 6000WAL | En Chuan Chemical Industries Co,. Ltd. | Polyester, TS | En Chuan |
| Lotader® 3410 | Arkema | EBA | Lotader® |
| Petrotene® PP A3 G40 HF CNZ0207 PH356 | Petropol Industry and Trade of Polymers LTDA | PP, Unspecified | Petrotene® PP |