NORYL GTX™ RNX130 resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AAg4wN_NORYL-GTX-RNX130-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% glass reinforced PPE+PS+PA alloy for automotive and nonautomotive applications. Recycle grade in black/gray only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Recycled Content |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 139 | MPa | ASTM D638 |
| Fracture | 139 | MPa | ASTM D638 |
| Tensile Elongation 2 | ASTM D638 | ||
| Yield | 5.0 | % | ASTM D638 |
| Fracture | 5.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 50.0mm span 3 | 8140 | MPa | ASTM D790 |
| 100mm span 4 | 7860 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| Fracture, 50.0mm span 5 | 186 | MPa | ASTM D790 |
| Fracture, 100mm span 6 | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 43 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 530 | J/m | ASTM D4812 |
| Instrumented Dart Impact (23°C, Total Energy) | 6.33 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 3.20mm | 252 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 3.20mm | 229 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 266 - 304 | °C | |
| Middle Temperature | 271 - 304 | °C | |
| Front Temperature | 277 - 304 | °C | |
| Nozzle Temperature | 282 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 76.7 - 121 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | Type 1, 5.0 mm/min |
| 2 . | Type 1, 5.0 mm/min |
| 3 . | 1.3 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.6 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sumitomo Silicone SI 9550 | Sumitomo Bakelite North America, Inc. | Silicone | Sumitomo Silicone |
| Texalan® 3 Series 398A | Austin Novel Materials Co. Ltd. | TPU-Polyester | Texalan® 3 Series |
| CompaDur® 125 GF 15 black (043) | DimeLika Plast GmbH | PBT+PET | CompaDur® |
| Hifax CA 1110 G4 1740 | LyondellBasell Industries | PP Copolymer | Hifax |
| ESTOPLAST EP 4030BL09 | Ester Industries Ltd. | PBT | ESTOPLAST EP |