Edgetek™ SF-30GF/15T NATURAL
| Category: | PPS , Polyphenylene Sulfide |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Edgetek™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | AAeVmE_EdgetekSF30GF15TNATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% Glass Fiber Reinforced and 15% PTFE Lubricated PPS Compounds |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.68 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11000 | MPa | ASTM D638 |
| Tensile Strength | 135 | MPa | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 175 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 110 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 260 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.75 mm | V-0 | UL 94 | |
| 1.5 mm | V-0 | UL 94 | |
| 3.0 mm | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 - 150 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 320 - 330 | °C | |
| Middle Temperature | 320 - 330 | °C | |
| Front Temperature | 320 - 330 | °C | |
| Mold Temperature | 140 - 160 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF 9203 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| TEREZ PC 1008 schwarz | TER HELL PLASTIC GMBH | PC | TEREZ PC |
| XYRON™ VT31V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| LNP™ COLORCOMP™ 420C compound | SABIC Innovative Plastics | PBT | LNP™ COLORCOMP™ |
| Hifax TYC 762PLS | LyondellBasell Industries | TPO (POE) | Hifax |