Braskem PE LF320
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Braskem |
| Trademark: | Braskem PE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A7WnEN_Braskem-PE-LF320.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LF320 is a Linear Low Density Polyethylene, copolymer of butene-1, produced by gas fase process. Developed for cast film extrusion. Films obtained with this product show a good processing performance balanced with good optical and mechanical properties as well as processability. Very low gel amount. It contains processing aid and antioxidant additives. Applications: Stretch films; liners; LDPE and HDPE blends and packages for general use. Process: Recommended processing conditions for film extrusion about 170 - 210 °C. The optimum processing conditions will vary according to the type of equipment used and cannot be considered as performance guarantee. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.919 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.7 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Break, 38 µm | 30.0 | MPa | |
| TD : Break, 38 µm | 20.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 38 µm | 1100 | % | |
| TD : Break, 38 µm | 1400 | % | |
| Flexural Modulus | ASTM D790 | ||
| 1% Secant, MD : 38 µm | 180 | MPa | |
| 1% Secant, TD : 38 µm | 230 | MPa | |
| Dart Drop Impact 1(38 µm) | 60 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 38 µm | 60 | g | |
| TD : 38 µm | 320 | g |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 38.0 µm) | 68 | ASTM D2457 | |
| Haze | 23 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | F50 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TITANPRO® PM201 | Lotte Chemical Titan (M) Sdn. Bhd. | PP Homopolymer | TITANPRO® |
| ADENE ACJB | A.D. Compound spa | PP Homopolymer | ADENE |
| HiFill® TPX-PMP-03032 | Techmer Engineered Solutions | PMP | HiFill® |
| Karina CLEAR PVC COMPOUND -E 70850/200-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| EnviroPro 3010GM | West Michigan Compounding | PP Homopolymer | EnviroPro |