Ultrason® E 1010
| Category: | PESU , Polyethersulfone |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultrason® E |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A6CnxG_Ultrason-E-1010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultrason E 1010 is an unreinforced, low viscosity injection molding PESU grade. It flows readily and offers outstanding heat resistance and dimensional stability. Applications Typical applications include automotive applications such as fuse encapsulation, connectors, heating system and headlight components and household applications such as microwave dishes and other applications requiring high heat resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (360°C/10.0 kg) | 150 | cm³/10min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 0.82 | % | |
| Flow | 0.79 | % | |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 2.2 | % | |
| Equilibrium, 23°C, 50% RH | 0.80 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness | 154 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 2650 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 85.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 6.8 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength | ISO 180 | ||
| -30°C | 7.0 | kJ/m² | |
| 23°C | 6.5 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 203 | °C | ISO 75-2/A |
| CLTE - Flow | 5.2E-5 | cm/cm/°C | |
| RTI Elec | UL 746 | ||
| 1.60 mm | 180 | °C | |
| 3.00 mm | 180 | °C | |
| RTI Imp | UL 746 | ||
| 1.60 mm | 180 | °C | |
| 3.00 mm | 180 | °C | |
| RTI Str | UL 746 | ||
| 1.60 mm | 190 | °C | |
| 3.00 mm | 190 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | IEC 60093 |
| Electric Strength | 37 | kV/mm | IEC 60243-1 |
| Dielectric Constant | IEC 60250 | ||
| 100 Hz | 3.90 | ||
| 1 MHz | 3.80 | ||
| Dissipation Factor | IEC 60250 | ||
| 100 Hz | 1.7E-3 | ||
| 1 MHz | 0.014 | ||
| Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.60 mm | V-1 | ||
| 3.00 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 130 to 150 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 340 to 390 | °C | |
| Mold Temperature | 140 to 180 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUMILITE® PL-1621 (Machining) | Sumitomo Bakelite Co., Ltd. | Phenolic | SUMILITE® |
| ULTEM™ AUT200 resin | SABIC Innovative Plastics | PEI | ULTEM™ |
| Delta N6-2500 | Delta Polymers | Nylon 6 | Delta |
| Geon™ 170 Series 179 | Mexichem Specialty Resins, Inc. | PVC Homopolymer | Geon™ 170 Series |
| ULTEM™ 2410R resin | SABIC Innovative Plastics | PEI | ULTEM™ |