NORYL™ WCD944 resin
| Category: | PPE+TPE , Polyphenylene Ether + TPE |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A62XyB_NORYL-WCD944-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Flexible and non-halogenated flame retardant extrusion grade intended for applications such as jacket of optical fiber cables. Flame retardant performance capable of meeting EN 50265-2-1 requirement. IEC60754 compliant. 94 Shore A hardness. Processing typically conducted on standard extrusion equipment. Wire tests conducted on 2.0 mm wire with 0.12 mm x 20 stranded copper conductor. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.998 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 16 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 30 sec) | 94 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Fracture | 22.0 | MPa | UL 1581 |
| Fracture 1 | 18.0 | MPa | ASTM D638 |
| Fracture, 136°C 2 | 23.0 | MPa | UL 1581 |
| Fracture | 18.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture | 310 | % | UL 1581 |
| Fracture 3 | 250 | % | ASTM D638 |
| Fracture, 136°C 4 | 240 | % | UL 1581 |
| Fracture | 220 | % | ISO 527-2/50 |
| Flexural Modulus 5 | |||
| 100mm span | 160 | MPa | ASTM D790 |
| -- | 140 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deformation 6(121°C) | 11 | % | UL 1581 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vertical Flame Test | PASSES | EN 50265-2-1 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 6.8E+15 | ohms·cm | ASTM D257 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (6.00 mm, Testing by SABIC) | V-0 | UL 94 | |
| Glow Wire Flammability Index (3.00 mm) | 960 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (3.00 mm) | 800 | °C | IEC 60695-2-13 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 75.0 - 85.0 | °C | |
| Drying Time | 5.0 - 7.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 180 - 220 | °C | |
| Cylinder Zone 3 Temp. | 220 - 250 | °C | |
| Cylinder Zone 5 Temp. | 220 - 250 | °C | |
| Melt Temperature | 220 - 250 | °C | |
| Die Temperature | 220 - 250 | °C |
| Extrusion instructions |
|---|
| Conductor Pre-heat Temperature: 25 - 120 °CCooling Water Air Gap: 100 - 200 mmCross-head Temperature: 220 - 250 °CDrying Time (Cumulative): 12 hrsExtruder Length/Diameter Ratio (L/D): 22:1 to 26:1Neck Temperature: 220 - 250 °CScreen Pack: 150 - 100Screw Speed: 15 - 85 rpmWater Bath Temperature: 15 - 60 °C |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | After 7 days |
| 3 . | Type 1, 50mm/min |
| 4 . | After 7 days |
| 5 . | 13 mm/min |
| 6 . | 250 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Viprene™ P90A-22U-NAT | Alliance Polymers & Services | TPV | Viprene™ |
| TYNE® Olefins W4301 | Tyne Plastics LLC. | HDPE | TYNE® Olefins |
| Electrafil® NY-7/EC NAT | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| Iupilon® CGH2010KR | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Karina IVORY PVC COMPOUND 70921-35/1-E-AC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |