GAPEX® HP RPP30EV05HB
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Ferro Corporation |
| Trademark: | GAPEX® HP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A4Vs26_GAPEX-HP-RPP30EV05HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| GAPEX®HP RPP30EV05HB is a polypropylene material, which contains a 30% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,. GAPEX®The main characteristics of HP RPP30EV05HB are: chemical coupling. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.5 | g/10 min | ASTM D1238 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.30 | % | ASTM D955 |
| Transverse flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 67.6 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 5.0 | % | ASTM D638 |
| Flexural Modulus | ASTM D790 | ||
| 1% secant : 23°C | 5120 | MPa | ASTM D790 |
| Tangent : 23°C | 5270 | MPa | ASTM D790 |
| Flexural Strength (Yield, 23°C) | 112 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 130 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 670 | J/m | ASTM D256 |
| Dart Drop Impact | 0.791 | J | ASTM D5420 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 159 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 146 | °C | ASTM D648 |
| Additional Information |
|---|
| Filler Content, ASTM D2584: 30% |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 71.1 - 82.2 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 221 - 238 | °C | |
| Middle Temperature | 227 - 243 | °C | |
| Front Temperature | 232 - 260 | °C | |
| Nozzle Temperature | 232 - 260 | °C | |
| Processing (Melt) Temp | 221 - 238 | °C | |
| Mold Temperature | 37.8 - 65.6 | °C | |
| Injection Rate | Slow-Moderate | ||
| Back Pressure | 0.138 - 0.345 | MPa | |
| Cushion | 5.08 - 12.7 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® HDP 510 | Marco Polo International, Inc. | HDPE | MARPOL® |
| Generic PP+EPDM | Generic | PP+EPDM | Generic |
| Hostacom TRC 352N R C12507 | LyondellBasell Industries | PP Copolymer | Hostacom |
| NHU-PPS 21610C/F | Zhejiang NHU Comp. Ltd. | PPS | NHU-PPS |
| LUVOCOM® 3-8896/WT/V-0 | LEHVOSS Group | Nylon 6 | LUVOCOM® |