Sindustris ABS LLG824
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | Sincerity Australia Pty Ltd. |
| Trademark: | Sindustris ABS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A4Ntwz_Sindustris-ABS-LLG824.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Sindustris ABS LLG824 is an Acrylonitrile Butadiene Styrene (ABS) material. It is available in Asia Pacific for extrusion. Primary attribute of Sindustris ABS LLG824: Low Gloss. Typical applications include:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.04 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 4.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.40 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 96 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(3.20 mm) | 2380 | MPa | ASTM D638 |
| Tensile Strength 2(Yield, 3.20 mm) | 37.3 | MPa | ASTM D638 |
| Tensile Elongation 3(Break, 3.20 mm) | 40 | % | ASTM D638 |
| Flexural Modulus 4(3.20 mm) | 1920 | MPa | ASTM D790 |
| Flexural Strength 5(3.20 mm) | 60.8 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.20 mm | 110 | J/m | |
| -30°C, 6.40 mm | 120 | J/m | |
| 23°C, 3.20 mm | 250 | J/m | |
| 23°C, 6.40 mm | 230 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 97.0 | °C | |
| 1.8 MPa, Unannealed, 6.40 mm | 90.0 | °C | |
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 6 |
| Optical | Nominal Value | Test Method | |
|---|---|---|---|
| Gloss (45°) | 30 | ASTM D2457 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 to 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.010 | % | |
| Melt Temperature | 200 to 250 | °C | |
| Die Temperature | 200 to 250 | °C |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 15 mm/min |
| 5 . | 15 mm/min |
| 6 . | Rate A (50°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILVER® SA-1304 | Guangdong Silver Age Sci & Tech. Co., Ltd | SBS | SILVER® |
| Telcar® OBC 2581B | Teknor Apex Company | TPE | Telcar® |
| Xuchuan A-9001T/B-8001D | Xuchuan Chemical (Suzhou) Co., Ltd | TPU-Polyester | Xuchuan |
| LEXAN™ EXL1494T resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ THERMOCOMP™ 2X98703 compound | SABIC Innovative Plastics | ETFE | LNP™ THERMOCOMP™ |