Ultramid® A3WG7 HP R01 BK20560
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A3dHoP_Ultramid-A3WG7-HP-R01-BK20560.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Ultramid A3WG7 HP R01 BK20560 is a 33% glass reinforced, heat stabilized, injection molding PA66 grade with excellent flow and surface finish. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.40 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.90 | -- | % | |
| Flow | 0.40 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 10700 | 7700 | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 198 | 131 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.1 | 5.1 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 9800 | 7190 | MPa | ISO 178 |
| Flexural Stress (23°C) | 287 | 205 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -30°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 14 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | |||
| -30°C | 60 | 60 | kJ/m² | |
| 23°C | 71 | 87 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180 | |||
| -40°C | 10 | 10 | kJ/m² | |
| 23°C | 12 | 13 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 259 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 244 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 260 | -- | °C | ISO 3146 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 280 to 305 | °C | |
| Mold Temperature | 80.0 to 90.0 | °C | |
| Injection Pressure | 3.45 to 10.3 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Spartech Polycom PP5413 B1 | Spartech Polycom | PP, Unspecified | Spartech |
| TECAFORM® HPV13 | Ensinger Inc. | Acetal (POM) Homopolymer | TECAFORM® |
| Talcoprene® 1530TC NATURALE | SO.F.TER. SPA | PP, Unspecified | Talcoprene® |
| Vi-Chem PVC VSR55D-80 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Geon™ HC 2155 | PolyOne Corporation | PVC, Flexible | Geon™ HC |