TECHNYL® C 246 V30 NATURAL
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Solvay Engineering Plastics |
| Trademark: | TECHNYL® C |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A3b2wP_TECHNYL-C-246-V30-NATURAL.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polyamide PA6, reinforced with 30 % of glass fibre, high impact strength, for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.32 | -- | g/cm³ | ISO 1183/A |
| Molding Shrinkage | Internal Method | |||
| Across Flow | 0.79 | -- | % | |
| Flow | 0.44 | -- | % | |
| Water Absorption (23°C, 24 hr) | 0.95 | -- | % | ISO 62 |
| Molding Shrinkage Isotropy | 0.560 | -- | Internal Method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 8200 | 5400 | MPa | ISO 527-2/1A |
| Tensile Stress (Break) | 140 | 90.0 | MPa | ISO 527-2/1A |
| Tensile Strain (Break) | 4.0 | 7.0 | % | ISO 527-2/1A |
| Flexural Modulus | 8000 | 5200 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -- | 18 | 30 | kJ/m² | |
| -30°C | 11 | -- | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -- | 86 | 100 | kJ/m² | |
| -30°C | 85 | -- | kJ/m² | |
| Notched Izod Impact Strength | 17 | 29 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 195 | -- | °C | ISO 75-2/Af |
| Melting Temperature | 222 | -- | °C | ISO 11357-3 |
| CLTE - Transverse (23 to 85°C) | 3.0E-5 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+13 | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
| Electric Strength | -- | 21 | kV/mm | IEC 60243-1 |
| Dissipation Factor | 0.020 | 0.10 | IEC 60250 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 22.0 to 230 | °C | |
| Middle Temperature | 225 to 235 | °C | |
| Front Temperature | 230 to 240 | °C | |
| Mold Temperature | 70.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 1C | BASF Corporation | Nylon 66/6 | Ultramid® |
| Chemlon® 109-14 GH | Teknor Apex Company (Chem Polymer) | Nylon 66 | Chemlon® |
| ENVIROPLAS® ENV13-NC820 | ENVIROPLAS®, Inc. | PC | ENVIROPLAS® |
| Idemitsu PS NS-300 | Idemitsu PS | PS (HIPS) | Idemitsu PS |
| OTECH TPE OTO9097 - Profile | OTECH Corporation | TPE | OTECH TPE |