Adiprene® LW 520
| Category: | PUR-Eth,aliphat , Polyurethane (Polyether, Aliphatic) |
| Manufacturer: | Chemtura |
| Trademark: | Adiprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A3EiIW_Adiprene-LW-520.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| ADIPRENE LW 520 is a polyether-based liquid casting urethane polymer, prepared with an aliphatic diisocyanate, that yields tough, high quality elastomers in the 90 durometer A hardness range when cured with methylene dianiline. It is readily processable by conventional hand and machine mixing techniques. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.3 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 88 to 92 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 7.07 to 8.45 | MPa | |
| 300% Strain | 19.3 to 25.9 | MPa | |
| Tensile Strength | 25.9 to 39.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 310 to 390 | % | ASTM D412 |
| Tear Strength (Split) | 9.6 | kN/m | ASTM D470 |
| Compression Set (70°C, 22 hr) | 60 to 70 | % | ASTM D395B |
| Bayshore Resilience | 38 to 42 | % | ASTM D2632 |
| Clash-Berg Modulus | ASTM D1043 | ||
| -57°C | 110 | MPa | |
| -40°C | 58.6 | MPa | |
| -18°C | 24.1 | MPa | |
| 24°C | 10.3 | MPa |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -60.0 | °C | ASTM D746 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 11 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Pot Life | 4.0 to 6.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Abrasion Index - NBS | 1100 to 1300 |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Curing Time (100°C) | 16 | hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® PPcompound 2609A | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Colorite G Series 10013G-015 | Colorite Polymers | PVC, Flexible | Colorite G Series |
| Ferro PP TPP20AF17HB NATURAL | Ferro Corporation | PP Homopolymer | Ferro PP |
| GERMAMID 6 GK 50 | Kunststoff-Kontor-Hamburg GmbH | Nylon 6 | GERMAMID |
| KOPA® KN333G20BL | Kolon Plastics, Inc. | Nylon 66 | KOPA® |