Borealis PP FSC65T30
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Borealis AG |
| Trademark: | Borealis PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | A1rNoL_Borealis-PP-FSC65T30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| FSC65T30 is a 30% mineral filled polypropylene compound intended for injection moulding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.15 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 5.0 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.95 | % | Internal Method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 55.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (1.00 mm) | 2800 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 23.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 3.5 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 3000 | MPa | ISO 178 |
| Flexural Stress | 38.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 2.5 | kJ/m² | |
| 23°C | 7.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 24 | kJ/m² | |
| 23°C | 67 | kJ/m² | |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -20°C | 3.0 | kJ/m² | |
| 23°C | 9.0 | kJ/m² | |
| Unnotched Izod Impact Strength | ISO 180/1U | ||
| -20°C | 21 | kJ/m² | |
| 23°C | 72 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 125 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/A |
| -- | 70.0 | °C | ISO 306/B |
| Melt Energy | 62.8 | kJ/kg | ISO 11357 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Fogging | < 2.0 | mg | DIN 75201 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Emission | < 50.0 | µgC/g | VDA 277 |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TP7CDZ (Series: EX) | KRAIBURG TPE | TPE | THERMOLAST® K |
| XYLEX™ X8303 resin | SABIC Innovative Plastics Europe | PC+Polyester | XYLEX™ |
| DESLON™ 6 DSC102GK | DESCO Co., Ltd. | Nylon 6 | DESLON™ 6 |
| LUVOCOM® 1105-8135/OR | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| ALTECH® PP-H FC 1000/576 | ALBIS PLASTIC GmbH | PP Homopolymer | ALTECH® PP-H |