HANWHA EVA 2240 is manufactured by DOW tubular high pressure process and designed for packaging film application.
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.929 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | Internal method |
| Vinyl Acetate Content | 9.5 | wt% | Internal method |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 50 µm | 26.2 | MPa | ASTM D882 |
| TD : Break, 50 µm | 22.6 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 50 µm | 230 | % | ASTM D882 |
| TD : Break, 50 µm | 700 | % | ASTM D882 |
| Dart Drop Impact (50 µm) | 400 | g | ASTM D1709A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 75.0 | °C | ASTM D1525 |
| Peak Melting Temperature | 94.0 | °C | Internal method |
| Freezing Point | 81 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm) | 4.4 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 170 | °C |
| Extrusion instructions |
|---|
| Blow-up Ratio: 2:1 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shanghai Ofluorine PVDF T-2 | Shanghai Ofluorine Chemical Technology Co., Ltd | PVDF | Shanghai Ofluorine PVDF |
| Siloxane Masterbatch MB50-002 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| HiFill® XRD PA66 0134 LE | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| LNP™ THERMOCOMP™ RF002XXH compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |
| Kepamid® 2350GFH | Korea Engineering Plastics Co., Ltd | Nylon 66 | Kepamid® |