Order Products : sales@su-jiao.com
VITAMIDE® AM10BK6734
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Jackdaw Polymers |
| Trademark: | VITAMIDE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9zkCIH_VITAMIDE-AM10BK6734.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VITAMIDE® AM10BK6734 is a Polyamide 66 (Nylon 66) product. It is available in Europe. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.14 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | 1.4 | % | Internal Method |
| Water Absorption (23°C, 24 hr) | 1.2 | % | ASTM D570, ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 80.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 30 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ASTM D790, ISO 178 |
| Flexural Stress | |||
| -- | 120 | MPa | ISO 178 |
| Break | 120 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 4.0 | kJ/m² | ISO 179 |
| Charpy Notched Impact Strength 1 | 4.00 | kJ/m² | ASTM D256 |
| Charpy Unnotched Impact Strength 2 | No Break | ASTM D256 | |
| Charpy Unnotched Impact Strength | No Break | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 225 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | °C | ASTM D648, ISO 75-2/A |
| Melting Temperature | 260 | °C | ASTM D2117, ISO 1218 |
| CLTE - Flow | 7.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+15 | ohms·cm | ASTM D257, IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vipel® F701-BID-08 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| 3M™ Dyneon™ PTFE Compound TF 2274 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ PTFE |
| Hanwha Total PP TB52T | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP, Unspecified | Hanwha Total PP |
| Huafon JF-P-8705 / JF-I-8805 (midsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| Medalist® MD-34065 | Teknor Apex Company | TPE | Medalist™ |