Dryflex® 502700S
| Category: | SEBS , Styrene Ethylene Butylene Styrene Block Copolymer |
| Manufacturer: | ELASTO |
| Trademark: | Dryflex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9zhIon_Dryflex-502700S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The 500S series is very favourable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mechanical properties, such as elongation, compression set, tensile and tear strength. The low density entails lower weight compared to the 600S and 660S series. Unfilled compounds are available in hardness from 0 Shore A to 55 Shore D in translucent and black colours but they can easily be coloured in any shade. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.890 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage | 0.80 to 2.0 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 70 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| -- | 9.00 | MPa | |
| 100% Strain | 3.00 | MPa | |
| 300% Strain | 4.00 | MPa | |
| Tensile Elongation (Break) | > 600 | % | ASTM D638 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tear Strength | 32.0 | kN/m | ASTM D624 |
| Compression Set (23°C, 72 hr) | 25 | % | ASTM D395 |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Service Temperature | -50 to 125 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 180 to 210 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 3499-3 X 117895 F | RTP Company | LCP | RTP |
| Mirakutoran® TPU E895 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Rotec® ABS 1001 FR V0/4 | ROMIRA GmbH | ABS | Rotec® ABS |
| LNP™ LUBRICOMP™ QAP22S compound | SABIC Innovative Plastics | Nylon 610 | LNP™ LUBRICOMP™ |
| Lupolen 4552D black | LyondellBasell Industries | HDPE | Lupolen |