LNP™ LUBRICOMP™ KP004 compound
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9yiZPI_LNP-LUBRICOMP-KP004-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP* KP004 is a compound based on Acetal Copolymer resin containing 20% PTFE/Silicone. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound KL-4540 Product Reorder name: KP004 |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.48 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 2.1 to 2.9 | % | |
| Across Flow : 24 hr | 2.1 to 2.9 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.18 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.43 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1830 | MPa | ASTM D638 |
| -- | 2020 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 43.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/5 |
| Break 3 | 43.0 | MPa | ASTM D638 |
| Break | 39.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 14 | % | ASTM D638 |
| Yield | 22 | % | ISO 527-2/5 |
| Break 5 | 30 | % | ASTM D638 |
| Break | 43 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2020 | MPa | ASTM D790 |
| -- 7 | 2080 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 60.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 63.0 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.25 | ||
| vs. Itself - Static | 0.14 | ||
| Wear Factor - Washer | 9.00 | 10^-10 in^5-min/ft-lb-hr | ASTM D3702 Modified |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 53 | J/m | ASTM D256 |
| 23°C 9 | 5.1 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 620 | J/m | ASTM D4812 |
| 23°C 10 | 42 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 3.90 | J | ASTM D3763 |
| -- | 1.06 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, Unannealed, 3.20 mm | 87.2 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 11 | 79.0 | °C | ISO 75-2/Af |
| CLTE | ASTM E831 | ||
| Flow : -40 to 40°C | 1.1E-4 | cm/cm/°C | |
| Transverse : -40 to 40°C | 1.1E-4 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 177 to 188 | °C | |
| Middle Temperature | 193 to 204 | °C | |
| Front Temperature | 210 to 221 | °C | |
| Processing (Melt) Temp | 199 to 216 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Monprene® SP-13188 | Teknor Apex Company | TPE | Monprene® |
| Exxtral™ Performance Polyolefin CNU017 | ExxonMobil Chemical | TPO | Exxtral™ Performance Polyolefin |
| Escorene™ Ultra FL 00119 | ExxonMobil Chemical | EVA | Escorene™ Ultra |
| Hylon® N1015HLFRA | Ravago Manufacturing Americas, LLC | Nylon 66 | Hylon® |
| Plenco 05118 (Transfer) | Plastics Engineering Co. | Phenolic | Plenco |