SCHULATEC® PEEK CF 30 NV 12
| Category: | PEEK , Polyetheretherketone |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULATEC® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9y22uB_SCHULATEC-PEEK-CF-30-NV-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30 % carbon fiber reinforced polyetheretherketone, low viscosity |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (400°C/2.16 kg) | 11 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 25400 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 218 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 1.7 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 21500 | MPa | ISO 178 |
| Flexural Stress | 319 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 8.5 | kJ/m² | ISO 180 |
| Unnotched Izod Impact Strength | 43 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load 1(1.8 MPa, Annealed) | 315 | °C | ASTM D648 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94, IEC 60695-11-10, -20 | ||
| 0.800 mm | V-0 | ||
| 1.60 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 150 | °C | |
| Drying Time | 3.0 to 6.0 | hr | |
| Rear Temperature | 360 to 370 | °C | |
| Middle Temperature | 380 to 390 | °C | |
| Front Temperature | 390 to 400 | °C | |
| Nozzle Temperature | 360 to 380 | °C | |
| Processing (Melt) Temp | 390 | °C | |
| Mold Temperature | 170 to 190 | °C |
| Note Message | |
|---|---|
| 1 . | Measured on annealed samples 3,2 mm thick, 200°C/2h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SOLARENE DH100 | Dongbu Hannong Chemical | PS (GPPS) | SOLARENE |
| NaturePlast NP DU 102 | NaturePlast | Nylon 1010 | NaturePlast |
| Nanjing Hongrui PA66 A1304 | Nanjing Hongrui Engineering Plastics Co., Ltd. | Nylon 66 | Nanjing Hongrui PA66 |
| Flontech® FT-COND2-1 | Guarniflon S.p.A. - Flontech Division | PTFE | Flontech® |
| IDI BMC Rosite 3550D | IDI Composites International | TS, Unspecified | IDI BMC |