Hostacom HRG 328T NAT
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9xahui_Hostacom-HRG-328T-NAT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Hostacom HRG 328T NAT is a low-emission / low-odor 30% glass coupled PP homopolymer with high flow, very high stiffness and low CLTE. Low creep under load at elevated temperatures. The product is designed for injection moulding of automotive parts and is available in natural colour. It is not intended for medical, phamaceutical and drinking water applications. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 12 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 120 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus - Secant | 7000 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 2.6 | % | ISO 527-2/50 |
| Flexural Modulus - Secant | 7200 | MPa | ISO 178 |
| Flexural Stress | 140 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 45 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 155 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 145 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 135 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Carbon Emission 1(120°C) | < 15.0 | µgC/g | VW Norm PV 3341 |
| Fogging 2(100°C) | < 1.0 | mg | DIN 75201B |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Odor 3(80°C) | < 4.00 | VW PV3200 |
| Note Message | |
|---|---|
| 1 . | 5 hr |
| 2 . | 16 hr |
| 3 . | 2 hr, Note 1-6 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tectron H2337 | TECTRON Systems Pte Ltd | TPV | Tectron |
| Dynaglide® DW 631 | DeWAL Industries | PTFE | Dynaglide® |
| Hostacom BB 1161 G | LyondellBasell Industries | PP Copolymer | Hostacom |
| Karina BLACK PVC COMPOUND 937-48/ 1-CY-IS-BZ | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Panlite® ML-5202ZHP | TEIJIN LIMITED | PC | Panlite® |