TITANLENE® LDF 200YZ
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Lotte Chemical Titan (M) Sdn. Bhd. |
| Trademark: | TITANLENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9wncHV_TITANLENE-LDF-200YZ.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LDF200YZ is a low density polyethylene resin for film extrusion. LDF200YZ has no slip and anti-block additives. LDF200YZ meets the U.S. Food and Drug Administration (FDA) criteria for food contact use as specified in 21 CFR 177.1520 (c) 2.1 & (c) 2.2. APPLICATIONS: T-shirt carrier bags, Display packaging, Light duty shrink film Characteristics: Good optical and good mechanical properties. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.922 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 30 | µm | |
| Secant Modulus | ASTM D882 | ||
| 1% Secant, MD : 30 µm, Blown Film | 206 | MPa | |
| 1% Secant, TD : 30 µm, Blown Film | 226 | MPa | |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 30 µm, Blown Film | 26.5 | MPa | |
| TD : Break, 30 µm, Blown Film | 21.6 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 30 µm, Blown Film | 310 | % | |
| TD : Break, 30 µm, Blown Film | 580 | % | |
| Dart Drop Impact (30 µm, Blown Film) | 60 | g | ASTM D1709 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 30 µm, Blown Film | 180 | g | |
| TD : 30 µm, Blown Film | 120 | g |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 95.0 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (30.0 µm, Blown Film) | 7.0 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 160 to 180 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 66 GF 20 GB 10 | Plastcom | Nylon 66 | SLOVAMID® 66 |
| Vydyne® R535J BK0701 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Badamid® LB70 GF40 TM-Z3 | Bada AG | Nylon 6 | Badamid® |
| Andur 3300 AS | Anderson Development Company | PUR-TDI | Andur |
| LUVOCOM® 1105-7714 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |