Clearflex® H&T CLH 196
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Versalis S.p.A. |
| Trademark: | Clearflex® H&T |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9wkuKF_Clearflex-H-T-CLH-196.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Clearflex H&T CLH 196 is a hexene copolymer linear low density polyethylene (C6-LLDPE), with antioxidants, suitable for cast film extrusion. Stretch films manufactured with Clearflex H&T CLH 196 have outstanding fracture mechanical properties, mainly Elmendorf tear strength along machine direction (MD) and puncture resistance. Moreover, the holding force is the key property of these films when used in automatic wrapping machines Main Application Clearflex H&T CLH 196 is recommended for production of super-power stretch films. Its properties, especially in terms of holding force and puncture resistance, make Clearflex H&T CLH 196 the ideal choice for packaging goods of irregular shape and for applications requiring a superior mechanical strength. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.916 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Cast Film) | > 0.50 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 23 | µm | |
| Film Thickness - Recommended / Available | 8 to 50µm | ||
| Tensile Modulus | ISO 527-3 | ||
| 1% Secant, MD : 23 µm, Cast Film | 140 | MPa | |
| 1% Secant, TD : 23 µm, Cast Film | 140 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 23 µm, Cast Film | 8.00 | MPa | |
| TD : Yield, 23 µm, Cast Film | 9.00 | MPa | |
| MD : Break, 23 µm, Cast Film | 38.0 | MPa | |
| TD : Break, 23 µm, Cast Film | 30.0 | MPa | |
| Tensile Elongation | ISO 527-3 | ||
| MD : Break, 23 µm, Cast Film | 600 | % | |
| TD : Break, 23 µm, Cast Film | 800 | % | |
| Dart Drop Impact 1(23 µm, Cast Film) | 300 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 23.0 µm | 140.0 | kN/m | |
| TD : 23.0 µm | 250.0 | kN/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Brittleness Temperature | < -70.0 | °C | ASTM D746 |
| Vicat Softening Temperature | 95.0 | °C | ISO 306/A |
| Melting Temperature | 123 | °C | Internal Method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 23.0 µm, Cast Film) | 92 | ASTM D2457 | |
| Haze (23.0 µm, Cast Film) | 2.5 | % | ISO 14782 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 220 to 270 | °C |
| Note Message | |
|---|---|
| 1 . | F50 |
| 2 . | Cast Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Tecoform® PO20 NL RM | Eurotec Engineering Plastics | Acetal (POM) Copolymer | Tecoform® |
| Sylvin 9216-60DUV Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Dutral® CO 034 | Versalis S.p.A. | EPDM | Dutral® |
| Lucky Enpla LMA1003 | Lucky Enpla Co LTD | Acrylic (PMMA) | Lucky Enpla |
| Hifax CB 1160 A BLACK | LyondellBasell Industries | PP Copolymer | Hifax |