Laramid D G/35-V0
| Category: | PPA , Polyphthalamide |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Laramid |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9weVV6_Laramid-D-G-35-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Semi-aromatic polyammide. Glass fibres. UL94 V-0 classified, with halogens. Good chemical resistance. Low moisture absorption. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.63 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.70 to 1.0 | % | |
| Flow : 2.00 mm | 0.30 to 0.55 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 16000 | MPa | |
| 60°C | 15500 | MPa | |
| 90°C | 15000 | MPa | |
| 120°C | 15000 | MPa | |
| 150°C | 10000 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 180 | MPa | |
| Break, 60°C | 170 | MPa | |
| Break, 90°C | 140 | MPa | |
| Break, 120°C | 135 | MPa | |
| Break, 150°C | 85.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.3 | % | |
| Break, 60°C | 1.3 | % | |
| Break, 90°C | 1.5 | % | |
| Break, 120°C | 1.7 | % | |
| Break, 150°C | 3.6 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 7.5 | kJ/m² | |
| 23°C | 6.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 25 | kJ/m² | |
| 23°C | 25 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 265 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 240 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 125 | °C | |
| Vicat Softening Temperature | 230 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 6.0E-6 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 350 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-0 | ||
| 1.50 mm | V-0 | ||
| 3.00 mm | V-0 | ||
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 1.00 mm | 960 | °C | |
| 2.00 mm | 960 | °C | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 1.00 mm | 800 | °C | |
| 2.00 mm | 800 | °C | |
| Oxygen Index | 42 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 310 to 330 | °C | |
| Mold Temperature | 130 to 160 | °C | |
| Injection Rate | Moderate |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S 32F 100 NAT | Radici Plastics | Nylon 6 | Radilon® |
| SABIC® PPcompound 7990E | Saudi Basic Industries Corporation (SABIC) | PP, Unspecified | SABIC® PPcompound |
| Laser+® C (C61A) | DAK Americas LLC | PET | Laser+® |
| Latimass 75/4-04 D009 | LATI S.p.A. | PBT | Latimass |
| LG ASA LI921NS | LG Chem Ltd. | ASA | LG ASA |