THERMOLAST® K TP6VCZ (Series: AD1/CS)
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | KRAIBURG TPE |
| Trademark: | THERMOLAST® K |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9vq9GR_THERMOLAST-K-TP6VCZ-Series-AD1-CS-.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
The AD1/CS Series is your material solution for applications with excellent adhesion to polar thermoplastics such as ABS, PC and PC/ABS as well as excellent compression set. The compounds are available in natural and black colors. Typical applications
Material advantages
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.10 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore A) | 60 | ISO 7619 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Yield) | 5.50 | MPa | ISO 37 |
| Tensile Elongation 2(Break) | 550 | % | ISO 37 |
| Tear Strength 3 | 15 | kN/m | ISO 34-1 |
| Compression Set 4 | ISO 815 | ||
| 23°C, 72 hr | 16 | % | |
| 70°C, 24 hr | 45 | % | |
| 100°C, 24 hr | 64 | % |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Adhesion to ABS | 6.0 | kN/m | Renault D41/1916 |
| Adhesion to PC | 16.5 | kN/m | Renault D41/1916 |
| Adhesion to PC/ABS | 13.5 | kN/m | Renault D41/1916 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 180 | °C | |
| Cylinder Zone 3 Temp. | 200 | °C | |
| Die Temperature | 220 | °C |
| Note Message | |
|---|---|
| 1 . | Type S2, 200 mm/min |
| 2 . | Type S2, 200 mm/min |
| 3 . | Method Bb, Angle (Nicked) |
| 4 . | Method A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| FHR Polypropylene P4C6Z-059 | Flint Hills Resources, LP | PP Homopolymer | FHR Polypropylene |
| EPIMIX PBT GV0 10 NC | EPSAN Plastik SAN. ve TiC. A.S. | PBT | EPIMIX |
| INELEC PPACF10 | Infinity LTL Engineered Compounds | PPA | INELEC |
| MAJORIS GFR320 | AD majoris | PP, Unspecified | MAJORIS |
| LNP™ STAT-KON™ RE0069S compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |