DOW™ LLDPE MP 1888.11 Copolymer
| Category: | LLDPE , Linear Low Density Polyethylene Resin |
| Manufacturer: | The Dow Chemical Company |
| Trademark: | DOW™ LLDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9vU5AB_DOW-LLDPE-MP-1888-11-Copolymer.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
| General Information | |
|---|---|
| Additive |
|
| Agency Ratings |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.926 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 1.6 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 51 | µm | |
| Film Puncture Resistance (51 µm) | 3.56 | J/cm³ | Internal method |
| Film strength | ASTM D882 | ||
| MD : 51 µm | 256 | J/cm³ | ASTM D882 |
| TD : 51 µm | 241 | J/cm³ | ASTM D882 |
| secant modulus | ASTM D882 | ||
| 2% secant, MD : 51 µm | 192 | MPa | ASTM D882 |
| 2% secant, TD : 51 µm | 246 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 51 µm | 12.1 | MPa | ASTM D882 |
| TD : Yield, 51 µm | 12.8 | MPa | ASTM D882 |
| MD : Fracture, 51 µm | 38.9 | MPa | ASTM D882 |
| TD : Fracture, 51 µm | 32.7 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Fracture, 51 µm | 750 | % | ASTM D882 |
| TD : Fracture, 51 µm | 770 | % | ASTM D882 |
| Dart Drop Impact (51 µm) | 170 | g | ASTM D1709B |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 51 µm | 800 | g | ASTM D1922 |
| TD : 51 µm | 1200 | g | ASTM D1922 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 108 | °C | ASTM D1525 |
| Melting Temperature (DSC) | 122 | °C | Internal method |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 50.8 µm) | 51 | ASTM D2457 | |
| Haze (50.8 µm) | 17 | % | ASTM D1003 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 202 - 216 | °C |
| Extrusion instructions |
|---|
| 吹塑薄膜的制造条件： 螺杆尺寸：2.5 英寸 (63.5 mm)；24:1 L/D 螺杆类型：带 Maddock Mixer 的 MC-4 模具间隙：40 密尔 (1.0 mm) 熔体温度：395-420°F (202-216°C) 输出：模具周长的 7 磅/小时/英寸 模具直径：6 英寸 放大比：2.5:1 螺杆速度：50 rpm 冷冻线高度：15 英寸 (381 mm) 脱离速度：75 fpm（23 米/分） |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen HP552R | LyondellBasell Industries | PP Homopolymer | Moplen |
| Vyncolit® SI 9042 | Vyncolit N.V. | Silicone | Vyncolit® |
| Clariant Nylon 6/6 66G25-L | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Kuraray Poval® PVA 124 | Kuraray Co., Ltd. | PVOH | Kuraray Poval® |
| LNP™ THERMOTUF™ VX00585 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOTUF™ |