Stanyl® TW371 is a Polyamide 46 (Nylon 46) material. It is available in Asia Pacific, Europe, or North America. Important attributes of Stanyl® TW371 are:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.25 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 2.0 | -- | % | |
| Flow | 2.0 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 3.2 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2900 | 1000 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 90.0 | 50.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 30 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 2600 | 900 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 7.0 | 15 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 150 kJ/m² | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength | ISO 180/1A | |||
| -40°C | 5.0 | 5.0 | kJ/m² | |
| 23°C | 7.0 | 14 | kJ/m² |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 190 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 1 | 295 | -- | °C | ISO 3146 |
| CLTE | ISO 11359-2 | |||
| Flow | 8.5E-5 | -- | cm/cm/°C | |
| Transverse | 1.1E-4 | -- | cm/cm/°C | |
| Thermal Index - 5000 hr | 152 | -- | °C | IEC 60216 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+14 | 1.0E+9 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 400 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Rear Temperature | 280 to 320 | °C | |
| Middle Temperature | 300 to 320 | °C | |
| Front Temperature | 300 to 320 | °C | |
| Nozzle Temperature | 300 to 320 | °C | |
| Processing (Melt) Temp | 310 to 320 | °C | |
| Mold Temperature | 80.0 to 120 | °C | |
| Injection Rate | Moderate-Fast | ||
| Back Pressure | 2.00 to 10.0 | MPa | |
| Screw Compression Ratio | 2.5:1.0 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEV-1138 | SHIN-A T&C | Epoxy | SHIN-A |
| TechnoFin TV 40 | TechnoCompound GmbH | PP, Unspecified | TechnoFin |
| XYRON™ VT31V | Asahi Kasei Chemicals Corporation | PPE+PS | XYRON™ |
| NatureFlex™ 23NE30 White | Innovia Films Ltd. | Cellulose, Regenerated | NatureFlex™ |
| APEX® 1581 | Teknor Apex Company | PVC, Flexible | APEX® |