Epiall® 2061B-1
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Epiall® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9tgTQF_Epiall-2061B-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Epiall 2061B-1 is a fiberglass and mineral reinforced epoxy molding compound, with excellent dimensional stability, good electrical insulation properties, and good strength. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.90 | g/cm³ | ASTM D792 |
| Apparent Density | 0.80 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow (Compression Molded) | 0.30 to 0.50 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.20 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 70 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 90.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 15900 | MPa | ASTM D790 |
| Flexural Strength (Break) | 138 | MPa | ASTM D790 |
| Compressive Strength | 230 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 37 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, Compression Molded) | 165 | °C | ASTM D648 |
| CLTE | ASTM E831 | ||
| Flow 1 | 1.9E-5 | cm/cm/°C | |
| Flow 2 | 2.9E-5 | cm/cm/°C | |
| Transverse 3 | 2.6E-5 | cm/cm/°C | |
| Transverse 4 | 4.1E-5 | cm/cm/°C | |
| RTI Elec | 130 | °C | UL 746 |
| RTI Imp | 130 | °C | UL 746 |
| RTI Str | 130 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 5 | ASTM D149 | ||
| -- 6 | 14 | kV/mm | |
| -- 7 | 13 | kV/mm | |
| Dielectric Constant 8(1 MHz) | 3.80 | ASTM D2520 | |
| Dissipation Factor 9(1 MHz) | 0.016 | ASTM D150 | |
| Arc Resistance | 180 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | V-0 | UL 94 |
| Note Message | |
|---|---|
| 1 . | Post Baked |
| 2 . | As Molded |
| 3 . | Post Baked |
| 4 . | As Molded |
| 5 . | Wet, 60 Hz |
| 6 . | Method A (Short-Time) |
| 7 . | Method B (Step-by-Step) |
| 8 . | Wet |
| 9 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Marlex® 1007 | Chevron Phillips Chemical Company LLC | LDPE | Marlex® |
| Clariant Nylon 6/6 PA-121 | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| COSMOPLENE® Z451G | TPC, The Polyolefin Company (Singapore) Pte Ltd | PP, Unspecified | COSMOPLENE® |
| Estane® 2103-90AENH TPU | Lubrizol Advanced Materials, Inc. | TPU-Polyether | Estane® |
| Packalloy LTO™ LTO | Spartech Plastics | Polyolefin, Unspecified | Packalloy |