Petrothene® GA605034
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Petrothene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9t3vLO_Petrothene-GA605034.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PETROTHENE GA 605 is a linear low density polyethylene designed for blown film applications requiring an enhanced combination of stiffness and strength. GA 605 can also be coextruded as a surface layer to enhance the clarity, gloss, printability and the heat seal of high molecular weight, high density polyethylene (HMW-HDPE) films. Applications include retail sacks, consumer can liners and packages, commercial and industrial packaging, as well as food packaging. GA 605-034 contains high levels of slip and antiblock. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.930 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 25 | µm | |
| secant modulus | ASTM D882 | ||
| 1% secant, MD : 25 µm | 338 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm | 403 | MPa | ASTM D882 |
| Tensile Strength | ASTM D882 | ||
| MD : Break, 25 µm | 60.0 | MPa | ASTM D882 |
| TD : Break, 25 µm | 37.2 | MPa | ASTM D882 |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 25 µm | 550 | % | ASTM D882 |
| TD : Break, 25 µm | 630 | % | ASTM D882 |
| Dart Drop Impact (25 µm, Blown Film) | 150 | g | ASTM D1709A |
| Total Energy Impact (25 µm, Blown Film) | 1.49 | J | ASTM D4272 |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm | 150 | g | ASTM D1922 |
| TD : 25 µm | 700 | g | ASTM D1922 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 25.4 µm, Blown Film) | 40 | ASTM D2457 | |
| Haze (25.4 µm, Blown Film) | 2.0 | % | ASTM D1003 |
| Additional Information |
|---|
| Film properties from 1.0 mil blown film produced with a blow up ratio of 2.5:1 and a 400°F melt temperature. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 204 - 232 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Siveras™ LX70M30H | Toray Resin Company | LCP | Siveras™ |
| ASTALON™ S2000R | Marplex Australia Pty. Ltd. | PC | ASTALON™ |
| Grivory® GM-4H | EMS-GRIVORY | Nylon 66+Nylon 6I/X | Grivory® |
| Karina WHITE PVC COMPOUND 806-10/ 42-B-RT-PO | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ QD000I compound | SABIC Innovative Plastics | Nylon 610 | LNP™ STAT-KON™ |