Firepel® K130-PTE-12
| Category: | Polyester Alloy , Polyester Alloy |
| Manufacturer: | AOC, L.L.C. |
| Trademark: | Firepel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9s2eac_Firepel-K130-PTE-12.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Firepel® Polyester Resin for Fire Retardant Applications Firepel® K130 series resin are designed forfire resistant applications where ASTM E 84 Class I flame and smoke development are required. Flammability of composite parts is dependent on the geometry of the part, degree of cure, reinforcement content, types of reinforcement, etc. It is the end user's responsibility to ensure that finished parts meet the required specifications. Published flammability properties should be used for comparison purposes only. Firepel® K130-AAA-00 is the concentrated highly brominated base resin that is used to manufacture the other versions. Firepel K130-AAA-00 can be used to manufacture specific tailored formulations. Fire Retardant Firepel® K130 PT, NN and TT series meet ASTM E 84 Class I flame and smoke requirements. Low VOC All Firepel K130 versions contain less than 35% styrene. Versatile Suitable for various fabricating methods such as hand lay-up, spray-up, filament winding, etc. The Firepel® K130 series molecular architecture provides an excellent balance of fire retardant, physical properties and cost. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.29 | g/cm³ | |
| Styrene Content | 33 | % |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Spread Index | 25.0 | ASTM E84 | |
| Smoke Developed | 135 | ASTM E84 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Exotherm | |||
| Gel to Peak | 10.0 | min | |
| Peak | 190 | °C | |
| Gel Time (25°C) 1 | 12.0 | min |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Thixotropic Index 2 | 3.00 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Barcol Hardness | 45 | ASTM D2583 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 4000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 73.8 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.2 | % | ASTM D638 |
| Flexural Modulus | 4070 | MPa | ASTM D790 |
| Flexural Strength | 106 | MPa | ASTM D790 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 90.0 | °C | ASTM D648 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB V-0 5V | UL 94 | |
| Oxygen Index | 39 | % | ASTM D2863 |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Mix Viscosity 3(25°C) | 550 | cP |
| Note Message | |
|---|---|
| 1 . | Gel time with 1.25% MEKP |
| 2 . | 2/20 rpm Thix Index |
| 3 . | Brookfield RV viscosity spindle 2 at 20 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® 8202 HS BK-102 | BASF Corporation | Nylon 6 | Ultramid® |
| Nypol® PA A3 BGE0072 NR319 | Petropol Industry and Trade of Polymers LTDA | Nylon 66 | Nypol® PA |
| Appeel® 72D811 | DuPont Packaging & Industrial Polymers | EA | Appeel® |
| INEOS LLDPE LL6130AA | INEOS Olefins & Polymers Europe | LLDPE | INEOS LLDPE |
| CYCOLAC™ FR15U resin | SABIC Innovative Plastics | ABS | CYCOLAC™ |