Vi-Chem PVC VNC107E
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Vi-Chem Corporation |
| Trademark: | Vi-Chem PVC |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9rgoV4_Vi-Chem-PVC-VNC107E.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Vi-Chem PVC VNC107E is a Polyvinyl Chloride material filled with 15% filler. It is available in North America. Typical application of Vi-Chem PVC VNC107E: Automotive |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.28 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 58 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Break) | 22.9 | MPa | ISO 37 |
| Thermal | Nominal Value | Test Method | |
|---|---|---|---|
| Cold Flexibility 2(-30°C) | No Cracks | GM 9503P |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Florida Weathering - Delta E 3 | 0.620 | ASTM G7 | |
| High Temperature Humidity Resistance | Pass | GM 9329P | |
| Mixed Fungal Resistance | Pass | GM 9328P | |
| Pink Stain | No Stains | GM 9303P | |
| Volatile Loss (105°C) | 1.3 | % | ASTM D1203 |
| Weather Resistance - Delta E 4 | 0.450 | SAE J1960 |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Bent around 50 mm mandrel |
| 3 . | 2 years |
| 4 . | 2500 kJ/m² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nipol® DN302 | Zeon Chemicals L.P. | NBR | Nipol® |
| ADENE NCZA | A.D. Compound spa | PP Homopolymer | ADENE |
| MAXATEL® AH500ALTF5-NC010 | Pier One Polymers, Inc. | Acetal (POM) Homopolymer | MAXATEL® |
| Sylvin 7833-90 White 1198 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| LGH 314 | LG Polymers India Pvt. Ltd. | PS (HIPS) | LGH |