LNP™ STAT-KON™ ME006 compound
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9rblxq_LNPSTATKONME006compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON* ME006 is a compound based on Polypropylene resin containing Carbon Fiber. Added features of this material include: Electrically Conductive. Also known as: LNP* STAT-KON* Compound MC-1006 Product reorder name: ME006 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 59.3 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 0.50 | % | ASTM D638 |
| Flexural Modulus | 11000 | MPa | ASTM D790 |
| Flexural Strength | 85.5 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 210 | J/m | ASTM D4812 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 193 - 204 | °C | |
| Middle Temperature | 216 - 227 | °C | |
| Front Temperature | 238 - 249 | °C | |
| Processing (Melt) Temp | 227 - 249 | °C | |
| Mold Temperature | 32.2 - 48.9 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ RN0612 resin | SABIC Innovative Plastics Europe | PPE+PS | NORYL™ |
| AKROMID® T4 GF 50 black (3661) | AKRO-PLASTIC GmbH | PPA | AKROMID® |
| Cleapact TS-50 E | DIC Corporation | PS Alloy | Cleapact |
| LACTEL® 85:15 DL-PLG | DURECT Corporation | PLA | LACTEL® |
| LNP™ LUBRICOMP™ Lexan_WR6300 compound | SABIC Innovative Plastics Asia Pacific | AES+PC+SAN | LNP™ LUBRICOMP™ |