Grilamid®2D 25 H HM black 9992 is a Polyamide 6/12 Copolymer (Nylon 6/12) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: extrusion. Grilamid®The main features of 2D 25 H HM black 9992 are:
Typical application areas include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.04 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturated, 23°C | 2.5 | -- | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 1.2 | -- | % | ISO 62 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Ball Indentation Hardness | 100 | 70.0 | MPa | ISO 2039-1 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 1900 | 1300 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 50.0 | 45.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | |||
| Yield | 5.0 | 17 | % | ISO 527-2 |
| Fracture | > 50 | > 50 | % | ISO 527-2 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 11 | 11 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 100 | 100 | kJ/m² | ISO 179/1eU |
| 23°C | No Break | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 115 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 55.0 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 217 | -- | °C | ISO 11357-3 |
| Linear thermal expansion coefficient | ISO 11359-2 | |||
| Flow | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.0E-4 | -- | cm/cm/°C | ISO 11359-2 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | -- | 1.0E+11 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+11 | 1.0E+11 | ohms·cm | IEC 60093 |
| Dielectric Strength | 35 | 35 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | -- | 600 | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification (0.8 mm) | HB | -- | IEC 60695-11-10, -20 |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Type | PA612, HHL, 22-020 | -- | ISO 1874 |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Manner Flexible PVC M1170 FR | Manner Plastics, L.P. | PVC, Flexible | Manner Flexible PVC |
| Maxxam™ F5134T4-1 | PolyOne Corporation | PP Homopolymer | Maxxam™ |
| TECHNIACE® TB-1801 | Nippon A&L Inc. | ABS+PBT | TECHNIACE® |
| Axiall PVC 22951 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| OTECH PVC OW137 - Cord Jacket | OTECH Corporation | PVC, Unspecified | OTECH PVC |