POLIGOM G/42
| Category: | EPDM , Ethylene Propylene Diene Terpolymer |
| Manufacturer: | Crosspolimeri S.p.A. |
| Trademark: | POLIGOM |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | 9qRIhY_POLIGOM-G-42.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
POLIGOM : is the trade mark of our crosslinkable EPDM compound ( phthalate plasticizers free ). POLIGOM G/42 : chemically crosslinkable elastomer for low voltage cable insulation and sheathing: suitable for G7. It is a conveniently grafted compound able to react in presence of moisture and of a catalyst. We normally suggest our catalyst type MAC/100 SCU. REACTION BETWEEN GRAFTING AND CATALYST: These two compounds, separately stored, must be mixed before starting extrusion in the ratio: GRAFTING/CATALYST 94/6 Certify : EN 50363-0 G7,BS 7655 GP4-GP5-GP6-GP7,HD 22.1 EI7 |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.900 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/5.0 kg) | 7.0 - 9.0 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 89 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | > 18.0 | MPa | IEC 60811 |
| Tensile Strain (Break) | > 450 | % | IEC 60811 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air (150°C, 168 hr) | 7.0 | % | IEC 60811 |
| Change in Tensile Strain at Break in Air (150°C, 168 hr) | -10 | % | IEC 60811 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset 1 | IEC 60811 | ||
| 250°C | 60 | % | IEC 60811 |
| Residual : 250°C | 0 | % | IEC 60811 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 190 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity (20°C) | > 4.0E+15 | ohms·cm | IEC 60502 |
| Dielectric Strength (20°C) | 39 | kV/mm | ASTM D149 |
| Additional Information |
|---|
| Crosslinking of the finished product is obtained by: Immersion of the bobbin in hot water at 85/90 °C for two hours (up to 3 mm thickness) Steam treatment at 0,15 bar for 5/6 hours. -Practically we suggest air crosslinking at natural temperatures and moisture: three or five days are enough. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 140 | °C | |
| Cylinder Zone 2 Temp. | 160 | °C | |
| Cylinder Zone 3 Temp. | 180 | °C | |
| Cylinder Zone 4 Temp. | 190 | °C | |
| Die Temperature | 205 | °C |
| Note Message | |
|---|---|
| 1 . | 20 N/cm² |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2655 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Mirathane™ E195F | Miracll Chemicals Co., Ltd. | TPU-Polyester | Mirathane™ |
| VITAMIDE® AY13 | A. Schulman Europe | Nylon 66 | VITAMIDE® |
| Domamid HT™ 7750R35H3 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |
| TECHNYL® C 52G2 MV25 GREY G 1783 CF | Solvay Engineering Plastics | Nylon 6 | TECHNYL® |